Photoelectrochemical Water Splitting and H2 Generation Enhancement Using an Effective Surface Modification of W-Doped TiO2 Nanotubes (WT) with Co-Deposition of Transition Metal Ions

Mohammadi, Tecush; Sharifi, Somayeh; Ghayeb, Yousef; Sharifi, Tayebeh; Momeni, Mohamad Mohsen (2022) Photoelectrochemical Water Splitting and H2 Generation Enhancement Using an Effective Surface Modification of W-Doped TiO2 Nanotubes (WT) with Co-Deposition of Transition Metal Ions. Sustainability, 14 (20). p. 13251. ISSN 2071-1050

PDF - Published Version - article Available under License Creative Commons Attribution. Download (4MB)

Abstract

W-doped TiO2 nanotube arrays (WT) were fabricated by in situ electrochemical anodization of titanium substrate. The results of the influence of different photo-deposited transition ions (CrxFe1−x, 0 ≤ x ≤ 1) on the surface of WT on photoelectrochemical (PEC) water splitting and H2 generation are presented. The crystallinities, structural, elemental, and absorption analysis were conducted by XRD, SEM, RAMAN, EDX, and UV–Vis absorption spectroscopy, which demonstrated anatase as the main crystalline phase of TiO2, and the existence of CrxFe1−x (nano)particles/film deposited on the surface of WT. The SEM images revealed that the deposition rate and morphology are highly related to the ratio of Cr and Fe ions. Under visible light illumination, the entire photoelectrodes showed a very good response to light with stable photocurrent density. PEC measurements revealed that the mixture of transition ions with a certain ratio of ions (Cr0.8Fe0.2–T) led to enhanced photocurrent density more than that of other modifiers due to decreasing charge recombination as well as improving the charge transfer. Moreover, PEC water splitting was conducted in an alkaline solution and the Cr0.8Fe0.2–T photoelectrode generated 0.85 mL cm−2 h−1 H2, which is over two times that of pristine WT.

Item Type:	Article
Uncontrolled Keywords:	TiO2 nanotubes; in situ electrochemical anodization; transition metals; hydrogen; water splitting
Subjects:	NATURAL SCIENCES > Chemistry
Divisions:	Division of Materials Chemistry
Depositing User:	Lorena Palameta
Date Deposited:	01 Dec 2023 15:41
URI:	http://fulir.irb.hr/id/eprint/8246
DOI:	10.3390/su142013251

Actions (login required)

View Item