Polaronic Conductivity in Iron Phosphate Glasses Containing B2O3

Pavić, Luka; Fazinić, Stjepko; Ertap, Hüseyin; Karabulut, Mevlüt; Moguš-Milanković, Andrea; Šantić, Ana (2020) Polaronic Conductivity in Iron Phosphate Glasses Containing B2O3. Materials, 13 (11). ISSN 1996-1944

[img]
Preview
PDF - Published Version - article
Available under License Creative Commons Attribution.

Download (4MB) | Preview

Abstract

We report on the electrical properties of glasses with nominal composition xB2O3 (100 x)40Fe2O3–60P2O5, x = 2 20, mol.. The conduction transport in these glasses is polaronic and shows a strong dependence on Fe2O3 content and polaron number density. The changes in DC conductivity are found not to be directly related to B2O3, however structural changes induced by its addition impact frequency-dependent conductivity. All glasses obey Summerfield and Sidebottom procedures of scaling conductivity spectra indicating that the polaronic mechanism does not change with temperature. An attempt to produce a super-master curve revealed that shape of the conductivity dispersion is the same for glasses with up to 15.0 mol.% B2O3 but differs for glass with the highest B2O3 content. This result could be related to the presence of borate units in the glass network. Moreover, the spatial extent of localized polaron motions increases with the decrease of polaron number density, however, this increase shows a larger slope than for previously reported iron phosphate glasses most probably due to the influence of B2O3 on glass structure and formation of polarons. While Summerfield scaling procedure fails, Sidebottom scaling yields a super-master curve, which indicates that polaronic hopping lengths also change with changing polaron number density in these glasses.

Item Type: Article
Uncontrolled Keywords: Iron phosphate glass ; Polaronic conductivity ; Glass–former oxide ; Structure–property relationship ; Impedance spectroscopy
Subjects: NATURAL SCIENCES > Physics
Divisions: Division of Experimental Physics
Division of Materials Chemistry
Projects:
Project titleProject leaderProject codeProject type
Detaljan uvid u mehanizme polaronske i ionske vodljivosti u oksidnoj staklo-(keramici)Šantić, AnaIP-2018-01-5425HRZZ
Depositing User: Stjepko Fazinić
Date Deposited: 07 Jan 2021 08:41
Last Modified: 07 Jan 2021 08:41
URI: http://fulir.irb.hr/id/eprint/6150
DOI: 10.3390/ma13112505

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

Contrast
Increase Font
Decrease Font
Dyslexic Font
Accessibility