Batch furnace CVD of pure boron layers on Si and GaN substrates for low-leakage-current diode fabrication

Vu, Thi Thanh Huong; Batenburg, Kevin M.; Aarnink, Antonius A.I.; Knežević, Tihomir; Liu, Xingyu; Nanver, Lis K. (2023) Batch furnace CVD of pure boron layers on Si and GaN substrates for low-leakage-current diode fabrication. JST - Engineering and Technology For Sustainable Development, 33 (2). pp. 29-35. ISSN 3093-3242

PDF - Published Version - article
Available under License Creative Commons Attribution.
Download (1MB)

Official URL: http://doi.org/10.51316/jst.165.etsd.2023.33.2.5

Abstract

Boron deposition on both n-Si and n-GaN in the temperature range 250 – 500 °C has been shown to form diodes with low saturation currents, i.e., electron injection from the n-substrate into the B-layer was efficiently suppressed. Moreover, down to 3-nm-thick B-layers on Si were shown to form a material barrier to Al, opening the possibility of fabricating Au-free gates for GaN HEMTs. Several different chemical- and physical-vapor deposition (CVD/PVD) methods for depositing B have been studied for fabricating p⁺n-like Si diodes, called PureB diodes, all with comparable results. In this paper, the deposition of B-layers from diborane in a CVD batch furnace system is evaluated, particularly for use as a barrier material to enable Al-contacting of GaN diodes. These Al-B diodes could provide an option for fabricating CMOS-compatible, low-leakage current diodes at industrially attractive high throughput. The bulk B has high resistivity, which, combined with the fact that non-uniformities in the nm range are typical due to gas depletion along the furnace tube, gives uncontrollable, often high diode series resistance. A simulation study shows that Al-B could, nevertheless, be used as a gate stack in HEMTs for low-frequency power applications.

Item Type:

Article

Uncontrolled Keywords:

batch furnace; CVD; boron layers; GaN; Si

Subjects:

NATURAL SCIENCES > Physics

Divisions:

Division of Materials Physics

Projects: