XRD and laser Raman spectroscopy investigation of the stability of low temperature t-ZrO2

Štefanić, Goran; Musić, Svetozar; Gržeta, Biserka; Popović, Stanko; Sekulić, Andreja (1998) XRD and laser Raman spectroscopy investigation of the stability of low temperature t-ZrO2. Croatica Chemica Acta, 71 (3). pp. 789-806. ISSN 0011-1643

[img] PDF - Published Version
Download (226kB)

Abstract

The influence of precipitation pH and the presence of Na+ impurities on the stability of metastable t-ZrO2 were investigated. Zirconia samples with a high t-ZrO2 phase content were crystallized from zirconium hydroxide precipitated at pH 13, 7 and 2.5. The obtained samples were subjected to the influence of temperature, pressure and gamma-irradiation. The influence of these treatments on the metastable t-ZrO2 were investigated using XRD and laser Raman spectroscopy. The results of phase analysis showed that the change in the pH of zirconium hydroxide precipitation significantly changed the sensitivity of the metastable t-ZrO2 to temperature and pressure. The metastable t-ZrO2 was most stable in the sample obtained from zirconium hydroxide precipitated at pH 2.5 and most unstable in the sample obtained from zirconium hydroxide precipitated at pH 7. The presence of Na+ impurities decreased the stability of metastable t-ZrO2. All the samples were shown to be stable under high gamma-irradiation. The capability of laser Raman spectroscopy for the quantitative analysis was examined by comparing the values of the m-ZrO2 volume fraction (nu(m)) obtained by this technique with the corresponding values obtained by XRD. It was concluded that the relation proposed by Clarke and Adar, J. Am. Ceram. Sec. 65 (1982) 284., was correct but the reliability of the nu(m) values estimated by the laser Raman spectroscopy was not high, especially in the region of 0.15 < nu(m) < 0.70. The reason for the low reliability in this region is discussed.

Item Type: Article
Uncontrolled Keywords: phase-transformation; thermal-behavior; zirconia; zro2; crystallization; hydroxide; ceo2; ph
Subjects: NATURAL SCIENCES > Chemistry
Divisions: Division of Materials Chemistry
Division of Materials Physics
Projects:
Project titleProject leaderProject codeProject type
Raspršenje svjetla, interakcije i dinamika materijeKrešimir Furić00980303MZOS
Sinteza i mikrostruktura metalnih oksida i oksidnih stakalaSvetozar Musić00980903MZOS
Depositing User: Goran Štefanić
Date Deposited: 27 Nov 2013 12:55
URI: http://fulir.irb.hr/id/eprint/1148

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

Contrast
Increase Font
Decrease Font
Dyslexic Font
Accessibility